Tig Welding Wires

A premium, multiple deoxidized, wireProduces high quality welds in most grades of carbon steelsE70S-2 is a triple deoxidized wire which provides defect free weld deposits when properly used on most carbon steels

The silicon addition improves puddle fluidity, producing an appealing bead profileIt is less crack sensitive on the 6XXX series than other welding alloysAll Position Welding

A general-purpose welding wire for fabrication of mild steelContains more deoxidizers that also provide better wetting, giving a flatter bead shape and the capability of faster travel speedsUsually used with 75/25 (argon/CO2) shielding gas or with higher...

A premium, multiple deoxidized, wireProduces high quality welds in most grades of carbon steelsE70S-2 is a triple deoxidized wire which provides defect free weld deposits when properly used on most carbon steels

Increases resistance to intergranular corrosionDual classification ensures the maximum carbon content is 0.03%All Position Welding

This copper-silicon alloy is used to weld similar composition base metals, brass, and to weld these copper alloys to steelSilicon bronze is also frequently used in GMAW "braze welding" of coated sheet steelsSilicon bronze base metals generally do not...

A premium, multiple deoxidized, wireProduces high quality welds in most grades of carbon steelsE70S-2 is a triple deoxidized wire which provides defect free weld deposits when properly used on most carbon steels

Maximum carbon content is 0.03%Use for high temperature service applicationsDesigned for flat and horizontal welding positions

A premium, multiple deoxidized, wireProduces high quality welds in most grades of carbon steelsE70S-2 is a triple deoxidized wire which provides defect free weld deposits when properly used on most carbon steels

Mild steel welding wire that contains high levels of manganese and silicon which produces high quality welds when used on dirty, oily or rusty steelThe high silicon content increases the fluidity of the weld pool, creating a smoother bead appearance...

Mild steel welding wire that contains high levels of manganese and silicon which produces high quality welds when used on dirty, oily or rusty steelThe high silicon content increases the fluidity of the weld pool, creating a smoother bead appearance...

Mild steel welding wire that contains high levels of manganese and silicon which produces high quality welds when used on dirty, oily or rusty steelThe high silicon content increases the fluidity of the weld pool, creating a smoother bead appearance...

Used for welding types 316 and 316L stainless steelsMaximum carbon content of 0.03% to reduce the possibility of formation of intergranular carbide precipitationPrimarily used for welding low carbon molybdenum bearing austenitic alloys

Used for welding types 316 and 316L stainless steelsMaximum carbon content of 0.03% to reduce the possibility of formation of intergranular carbide precipitationPrimarily used for welding low carbon molybdenum bearing austenitic alloys

Used for welding types 316 and 316L stainless steelsMaximum carbon content of 0.03% to reduce the possibility of formation of intergranular carbide precipitationPrimarily used for welding low carbon molybdenum bearing austenitic alloys

Used for welding types 316 and 316L stainless steelsMaximum carbon content of 0.03% to reduce the possibility of formation of intergranular carbide precipitationPrimarily used for welding low carbon molybdenum bearing austenitic alloys

Used for welding types 316 and 316L stainless steelsMaximum carbon content of 0.03% to reduce the possibility of formation of intergranular carbide precipitationPrimarily used for welding low carbon molybdenum bearing austenitic alloys

Used for welding types 316 and 316L stainless steelsMaximum carbon content of 0.03% to reduce the possibility of formation of intergranular carbide precipitationPrimarily used for welding low carbon molybdenum bearing austenitic alloys

Used for welding types 316 and 316L stainless steelsMaximum carbon content of 0.03% to reduce the possibility of formation of intergranular carbide precipitationPrimarily used for welding low carbon molybdenum bearing austenitic alloys

Used for welding types 316 and 316L stainless steelsMaximum carbon content of 0.03% to reduce the possibility of formation of intergranular carbide precipitationPrimarily used for welding low carbon molybdenum bearing austenitic alloys

Used for welding types 316 and 316L stainless steelsMaximum carbon content of 0.03% to reduce the possibility of formation of intergranular carbide precipitationPrimarily used for welding low carbon molybdenum bearing austenitic alloys

Used for welding types 316 and 316L stainless steelsMaximum carbon content of 0.03% to reduce the possibility of formation of intergranular carbide precipitationPrimarily used for welding low carbon molybdenum bearing austenitic alloys

Used for welding types 316 and 316L stainless steelsMaximum carbon content of 0.03% to reduce the possibility of formation of intergranular carbide precipitationPrimarily used for welding low carbon molybdenum bearing austenitic alloys

Used for welding cast and wrought alloys of similar composition as well as dissimilar metals including stainless to mild steelsCan be used for welding high strength steelsVery high ferrite

Similar to type 309 except for the carbon content being lower than .03%Extra low carbon content provides good resistance to carbide precipitation and intergranular corrosionWorks well for dissimilar joints that undergo heat treatment

Similar to type 309 except for the carbon content being lower than .03%Extra low carbon content provides good resistance to carbide precipitation and intergranular corrosionWorks well for dissimilar joints that undergo heat treatment

Similar to type 309 except for the carbon content being lower than .03%Extra low carbon content provides good resistance to carbide precipitation and intergranular corrosionWorks well for dissimilar joints that undergo heat treatment

Similar to type 309 except for the carbon content being lower than .03%Extra low carbon content provides good resistance to carbide precipitation and intergranular corrosionWorks well for dissimilar joints that undergo heat treatment

Similar to type 309 except for the carbon content being lower than .03%Extra low carbon content provides good resistance to carbide precipitation and intergranular corrosionWorks well for dissimilar joints that undergo heat treatment

Similar to type 309 except for the carbon content being lower than .03%Extra low carbon content provides good resistance to carbide precipitation and intergranular corrosionWorks well for dissimilar joints that undergo heat treatment

Same analysis as ER308L but with a higher silicon contentHigher silicon content improves arc stability, bead appearance and wetting actionProduces exceptionally smooth welds for applications that require a good cosmetic appearancePrimarily used with...

Same analysis as ER308L but with a higher silicon contentHigher silicon content improves arc stability, bead appearance and wetting actionProduces exceptionally smooth welds for applications that require a good cosmetic appearancePrimarily used with...

Used for welding types 316 and 316L stainless steelsMaximum carbon content of 0.03% to reduce the possibility of formation of intergranular carbide precipitationPrimarily used for welding low carbon molybdenum bearing austenitic alloys

Used for welding types 316 and 316L stainless steelsMaximum carbon content of 0.03% to reduce the possibility of formation of intergranular carbide precipitationPrimarily used for welding low carbon molybdenum bearing austenitic alloys

Features molybdenum grade that offers enhanced corrosion resistanceSuitable for all welding positions, except vertical down, has flux coating that renders smoother arc transfer and a self-peeling slag for easy removalLow carbon levels to eliminate...

Features molybdenum grade that offers enhanced corrosion resistanceSuitable for all welding positions, except vertical down, has flux coating that renders smoother arc transfer and a self-peeling slag for easy removalLow carbon levels to eliminate...

Features molybdenum grade that offers enhanced corrosion resistanceSuitable for all welding positions, except vertical down, has flux coating that renders smoother arc transfer and a self-peeling slag for easy removalLow carbon levels to eliminate...

Used for welding types 316 and 316L stainless steelsMaximum carbon content of 0.03% to reduce the possibility of formation of intergranular carbide precipitationPrimarily used for welding low carbon molybdenum bearing austenitic alloys

Used for welding types 304, 304L, 308 and 308L stainless steelsVery similar to type 308 but has a carbon content held to a max of 0.03% to avoid carbide precipitation

Extra low carbon electrode for the welding of type 304L, 321, and 347 stainless steelsControlled ferrite in the weld deposit gives excellent notch toughness at cryogenic temperaturesDeposits a max of 4% carbon in the weld metal to minimize the formation...